ENISO 12543 - 4 Glass in building -Laminated glass and laminated safety glass -Part 4: Test methods for durability Clause 5 High-temperature test
AS/NZS2208 Safety glazing materials in buildings Appendix F Boil Test
GB15763.3 Safety glazing materials in building Part 3:Laminated glass Clause 7.8Heat resistance test
ANSIZ97.1 Safety Glazing Materials Used in Buildings - Safety Performance Specifications and Methods of Test - Clause 5.3.2 ( 1 ) Boil Test
Power:220V 50Hz 3Kw (Customized)
Outside Size: 430mm*290mm*575 mm
Inner Size: 400mm*255mm*480mm
Atmost 6 samples with 300mm*300mm
Determiningthe effect of exposure of safety glazing materials to temperature and humiditycondition by boiling
Specimens are immerse in hot water and boilingwater for specified period of time and inspect bubbles and others defects
The apparatus include two water baths, each of sufficient size to hold the testspecimen fully immersed vertically on edge for the duration test.
Three specimen of size 300mm*300mm manufacture in a manner identical with impact testspecimens and of like thickness shall be tested.
These specimens may be cut from production samples of the size and thickness submitted for impact testing.
For heat strengthened or toughened laminated glass, test specimen may be cut from asimilar original sheet of annealed laminated glass
Immerse the specimens vertically on edge in a bath of water maintained at a temperature of 66 °C for 3 min
Quickly transfer the specimens to a bath of water maintain at boiling point. Immerse the specimens vertically on edge for 2 h
Remove the specimens and examine for the bubbles and others defects